三维NZSPO/PAN-[PEO-NaTFST]复合钠离子电池固体电解质
|
刘当玲 1( ), 王诗敏 1, 高智慧 1, 徐露富 1, 夏书标 2( ), 郭洪 1( )
|
Properties of three-dimensional NZSPO/PAN-[PEO-NATFST] sodium-battery-composite solid electrolyte
|
Dangling LIU 1( ), Shimin WANG 1, Zhihui GAO 1, Lufu XU 1, Shubiao XIA 2( ), Hong GUO 1( )
|
|
图6. (a) 60 ℃下,通过线性扫描伏安法以0.1 mV/s的扫描速率测定2NZSPO/PAN-[PEO15-NaTFSI]复合固体电解质的电化学稳定窗口;(b) NVP/SPE/Na和NVP/CPE/Na电池在0.1 C、80 ℃下的首次充电/放电曲线
|
Fig. 6. (a) electrochemical stability window of 2NZSPO/PAN-[PEO15-NaTFSI] composite solid electrolyte was measured by linear scanning voltammetry at a scan rate of 0.1 mV/s at 60 ℃; (b) first charge/discharge curves of NVP/SPE/Na and NVP/CPE/Na batteries at 0.1 C and 80 ℃
|
|
|
|
|