Co0.1Fe0.9S2@Li7P3S11正极材料的制备及其在全固态锂电池中的性能
|
蒋苗 1,2( ), 万红利 1, 刘高瞻 1,2, 翁伟 1,2, 王超 1, 姚霞银 1,2( )
|
Co0.1Fe0.9S2@Li7P3S11composite cathode material for all-solid-state lithium batteries
|
Miao JIANG 1,2( ), Hongli WAN 1, Gaozhan LIU 1,2, Wei WENG 1,2, Chao WANG 1, Xiayin YAO 1,2( )
|
|
图5. (a) Co0.1Fe0.9S2@Li7P3S11和(b) FeS2在1.0~3.0 V的恒流充放电曲线;(c) Co0.1Fe0.9S2@Li7P3S11和FeS2在1.0~3.0 V、200 mA/g下的循环曲线;(d) Co0.1Fe0.9S2@Li7P3S11和FeS2首圈和循环100圈后的EIS曲线
|
Fig. 5. Galvanostatic charge-discharge profiles of (a) Co0.1Fe0.9S2@Li7P3S11 and (b) FeS2 cathode in the range of 1.0~3.0 V; (c) cycling stability of Co0.1Fe0.9S2@Li7P3S11 and FeS2 cathode in the range of 1.0~3.0 V at200 mA/g; (d) nyquist plots for Co0.1Fe0.9S2@Li7P3S11 and FeS2 cathode after 1st and 100th cycles
|
|
|
|
|