基于无机钠离子导体的固态钠电池研究进展
|
彭林峰, 贾欢欢, 丁庆, 赵宇明, 谢佳, 程时杰
|
Research progress of solid-state sodium batteries using inorganic sodium ion conductors
|
Linfeng PENG, Huanhuan JIA, Qing DING, Yuming ZHAO, Jia XIE, Shijie CHENG
|
|
表1 基于氧化物钠离子固态电解质的中低温固态电池总结
|
Table 1 Summary of solid-state batteries based on oxide sodium solid electrolytes
|
|
固态电池 | 循环圈数 | 容量保持 | 温度 | 参考文献 |
---|
Na|β?-Al2O3|NaTi3(PO4)3 | 50圈(0.1 C) | 100 mA·h/g | RT | [25] | | Na|β?-Al2O3-PVDF-HFP|Na3V2(PO4)3 | 1000圈(1 C) | 90 mA·h/g | RT | [26] | | Na|β?-Al2O3|Na0.66Ni0.33Mn0.67O2-IL | 10000圈(6 C) | 90% | 70 ℃ | [27] | | Na|LE-β?-Al2O3-LE|S-C | 104圈(1/64 C) | 521 mA·h/g | RT | [28] | | Na-Sn|β?-Al2O3|PTO-PEO-C | 50圈(0.1 C) | 80% | 60 ℃ | [29] | | Na|β?-Al2O3|NiCl2 | 350圈(20~30 mA) | 355 W·h/kg | 190 ℃ | [31] | | Na|CPMEA/Na3Zr2Si2PO12|NaTi2(PO4)3 | 70圈(0.2 C) | 100 mA·h/g | 65 ℃ | [33] | | Na|Na3.1Zr1.95Mg0.05Si2PO12|Na0.9Cu0.22Fe0.3Mn0.48O2 | 100圈(0.5 C) | 57.9 mA·h/g | RT | [35] | | Na|0.1Ca-NZSP|Na3V2(PO4)3 | 450(1 C) | 94.9 mA·h/g | 25 ℃ | [36] | | Na|IL/Na3.3Zr1.7La0.3Si2PO12|Na3V2(PO4)3 | 10000圈(10 C) | 90 mA·h/g | RT | [39] | | Na|SN-Na3Zr2Si2PO12|Na3V2(PO4)3 | 50圈(20 mA/g) | 62.23 mA·h/g | RT | [41] | | Na|Na3.4Zr2Si2.4P0.6O12|Na3V2(PO4)3 | 100圈(0.6 C) | 96.5 mA·h/g | 25 ℃ | [42] | | NVPF|NYSO-PEO-SSE| Na3V2(PO4)3 | 50圈(1 C) | 89% | 60 ℃ | [45] | | Na|Na3Zr2Si2PO12|Na2MnFe(CN)6 | 200圈(0.5 C) | 89.2% | 60 ℃ | [46] | | Na|CPE-NZMSPO|Na3V2(PO4)3 | 120圈(0.1 C) | 106.1 mA·h/g | 80 ℃ | [47] | |
|
|
|