钠离子电池聚合物电解质研究进展
|
高舒, 周敏, 韩静, 过聪, 谭媛, 蒋凯, 王康丽
|
Progress on polymer electrolyte in sodium ion batteries
|
Shu GAO, Min ZHOU, Jing HAN, Cong GUO, Yuan TAN, Kai JIANG, Kangli WANG
|
|
表1 基于不同聚合物固态电解质离子电导率与循环圈数对比
|
Table 1 Comparison of ionic conductivities and cycle numbers of solid polymer electrolyte in various cell systems
|
|
电解质材料 | 测试温度/℃ | 电导率/S·cm-1 | 测试体系 | 循环圈数 | 参考文献 |
---|
PEO/NaTf | 90 | — | Na||Na0.9CO2 | 300 | [11] | P(EO)20/NaFSI | 80 | 4.1×10-4 | Na||Na0.67Ni0.33MnO2 | 50 | [12] | Na||Na3V2(PO4)3 | 30 | PVA/NaBr | 30 | 1.362×10-6 | Na||I2 | — | [13] | PTMC/NaTFSI | 60 | >10-6 | Na||PB | 8 | [14] | PEO/Na-CMC/NaClO4 | 60 | >10-5 | Na||NaFePO4 | 20 | [15] | PEO/TiO2/NaClO4 | 60 | 2.62×10-5 | Na||Na2/3Co2/3Mn1/3O2 | 25 | [16] | PMA/PEG/NaClO4/α-Al2O3 | 70 | 1.46×10-4 | Na||Na3V2(PO4)3 | 350 | [17] | PEO/PEG/NaClO4 | 30 | 3.4×10-6 | Na||MnO2 | — | [18] | PCL/PTMC/NaFSI | 22 | 3.9×10-6 | HC||Na2-xFe(Fe(CN)6) | 120 | [19] | PFSA/Na+ | 25 | 1.59×10-4 | Na||PB | 160 | [20] | B-PCPE | 20 | 3.6×10-4 | HC|| NaNi1/3Fe1/3Mn1/3O2 | 120 | [21] |
|
|
|